dc.descriptionรายงานการวิจัย -- มหาวิทยาลัยเทคโนโลยีราชมงคลพระนคร, 2561en_US
dc.description.abstractThe results of the study on the optimum temperature for baking soda extinguishers were investigated. B9R-3-EMERALD Using brass material in experiments. It was found that the temperature of 750˚C was good for 48% of the workpiece, 52% was found that the workpiece was damaged at the surface of the work very porous at the surface. Caused by the heat of metal water pouring into contact with the moisture of the mold, resulting in gas. High temperature of metal water Or eliminate gas in metal water is not exhausted. The workpiece is not suitable at a temperature of 800 ° C with a good workpiece of 76%. The workpiece loses 24%. The workpiece loses less punch at the lower porosity as well at 750˚C in temperature. 850˚C workpiece, 96% workpiece, 4% workpiece, the workpiece is almost out. It is less than 750˚C and 800˚C at porosity. And at 900˚C, the workpiece is 100% of the workpiece 0%. The workpiece is the best. Workpiece waste from the minimum. The test results make the temperature at 900 ° C is the cleanest casing temperatureen_US
dc.description.sponsorshipRajamangala University of Technology Phra Nakhonen_US
dc.language.isothen_US
dc.subjectBurningen_US
dc.subjectการเผาไหม้en_US
dc.subjectTemperatureen_US
dc.subjectอุณหภูมิen_US
dc.subjectMaster resinen_US
dc.subjectมาสเตอร์เรซิ่นen_US
dc.titleThe temperature heat for burning to eliminate the master resin plaster casting jewelryen_US
dc.title.alternativeการศึกษาอุณหภูมิความร้อนที่เหมาะสมต่อการอบเผาขจัดต้นแบบเรชิ่นในเบ้าปูนหล่อเครื่องประดับen_US
dc.typeResearch Reporten_US
dc.contributor.emailauthorky_1942@hotmail.comen_US
dc.contributor.emailauthorarit@rmutp.ac.then_US


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record